칼슘이 용출된 콘크리트의 공극 구조 및 강도 특성

Characteristics of Pore Structures and Compressive Strength in Calcium Leached Concrete Specimens
콘크리트학회 논문집 제23권 제5호, 2011.10, 647-656 (10 pages)
인용정보 복사
Quick View Quick View
구매하기 6,000원
인용하기
이용수 : 60건
피인용수 : 0건
분야내 활용도 : 12%
자세히 보기 >

· 이용수 : 2010년부터 집계한 원문다운로드수

· 피인용수 : DBpia 논문 가운데 해당 논문을 인용한 논문수

· 분야내 활용도 : 최근 24개월간 DBpia 이용수를 기준으로 산출 / 0%에 가까울 수록 활용도가 높고, 100%에 가까울 수록 활용도가 낮음

초록
In radioactive waste repositories constructed in underground, concrete member could be in contact with groundwater for a long time. However, this pure water creates concentration gradients which lead to the diffusion of Ca ions from the pore water and the degradation of underground concrete. Therefore, this study is aimed at investigating the alteration of pore structure and loss of compressive strength associated with dissolution. The results showed that as the leaching period became longer, the pore volume within 50 nm to 500 nm in diameter is greatly increased. Also, the volume of pores larger than 200 nm rapidly increased during initial leaching time and those below 200 nm gradually increased. Furthermore, the compressive strength gradually decreased with increase of degraded thickness. The residual strength of the degraded concrete with OPC was in the range of 33% to 58%.

방사성 폐기물 처분 시설과 같은 지하 구조물의 콘크리트 부재가 장기간에 걸쳐 지하수(이온교환수)와 접촉하면 이온교환수와 공극수 사이에 농도구배가 발생한다. 이로 인해 공극수로부터 칼슘이온이 용출되고, 콘크리트의 열화가 진행된다. 따라서 이 연구에서는 콘크리트의 칼슘 용출에 의한 내부공극 구조의 변화를 분석하고, 열화된 콘크리트의 강도 특성을 평가하고자 하였다. 연구 결과, 콘크리트의 칼슘이온이 용출됨에 따라 50~500 nm 크기의 공극들이 상당히 증가하게 되며, 용출 초기에는 200 nm 크기 이상의 공극들이 급격히 증가하고 이후에는 200 nm 크기 이하의 공극들이 증가하는 것으로 나타났다. 칼슘이 용출된 두께가 증가함과 더불어 압축강도는 감소하였으며, 칼슘이 용출된 OPC 콘크리트의 잔류강도는 대략 33~58% 정도로 나타났다.

목차
ABSTRACT
1. 서론
2. 실험 계획 및 방법
3. 실험 결과 및 분석
4. 결론
참고문헌
요약
키워드
참고문헌 (12)

현재 논문의 참고문헌을 찾아 신청해주세요!

  1. Carde, C. , 1997 , Use of Ammonium Nitrate Solution to Simulate and Accelerate the Leaching of Cement Pastes due to Deionized Water , Magazine of Concrete Research 49 (181) : 295 ~ 301

  2. Haga, K. , 2005 , Change in Pore Structure and Composition of Hardened Cement Paste During the Process of Dissolution , Cement and Concrete Research 35 (5) : 943 ~ 950

  3. Haga, K. , 2005 , Effect of Porosity on Leaching of Ca from Hardened Ordinary Portland Cement Paste , Cement and Concrete Research 35 (9) : 1764 ~ 1775

  4. Carde, C , 1997 , Effect of ITZ Leaching on Durability of Cement-Based Materials , Cement and Concrete Research 27 (7) : 971 ~ 978

  5. Saito, H , 2000 , Leaching Tests on Different Mortars Using Accelerated Electrochemical Method , Cement and Concrete Research 30 (11) : 1815 ~ 1825

  6. Skoczylas, F. , 2007 , Experimental Study of Accelerated Leaching on Hollw Cylinders of Mortar , Cement and Concrete Research 37 (1) : 71 ~ 78

  7. Torrenti, J. M. , 2007 , Chemo- Mechanical Coupling Behaviour of Leached Concrete Part I: Experimental Results , Nuclear Engineering and Design 237 (20) : 2083 ~ 2089

  8. ASTM International , 2010 , Standard Test Method for Microscopical Determination of Parameters of the Air-Void System in Hardened Concrete , ASTM C 457, West Conshohocken, PA : 1022 ~

  9. ASTM International , 2007 , Standard Test Method for Determining Pore Volume Distribution of Catalysts by Mercury Intrusion Porosimetry , ASTM D 4284, West Conshohocken, PA : 650 ~

  10. 이창수 , 2004 , 양생온도와 재령에 다른 콘크리트의 공극구조 특성 변화와 압축강도와의 관계 , 대한토목학회 논문집A 24 (6a) : 1145 ~ 1150

  • 처음
  •  
  • 이전
  •  
  • 1
  •  
  • 2
  •  
  • 다음
  •  
  • 마지막
인용된 논문 (0)

알림서비스 신청하고 '인용된 논문' 정보를 메일로 확인 하세요!

해당 논문은 인용된 논문 정보가 없습니다.

제 1 저자의 다른 논문 (111)

양은익 식별저자 저자의 상세정보를 확인해 보세요.

권호 내 다른 논문 (18)

콘크리트학회 논문집 제23권 제5호 의 상세정보를 확인해 보세요.

  • 처음
  •  
  • 이전
  •  
  • 1
  •  
  • 2
  •  
  • 다음
  •  
  • 마지막
추천 논문 (8)

DBpia 추천논문과 함께 다운받은 논문을 제공합니다. 논문 초록의 텍스트마이닝과 이용 및 인용 관계 분석을 통해 추천해 드리는 연관논문을 확인해보세요.

DBpia 추천논문

더 많은 추천논문을 확인해 보세요!

함께 다운받은 논문

지표

이용현황

· 이용수

· 이용순위 상위 Top3

자세히 보기 >
No 상위 이용이관 이용수
1 강릉원주대학교 8
2 세종대학교 7
3 충남대학교 3

활용도

· 활용지수

· 논문의 활용도 추이 (주제분야 기준)

자세히 보기 >

: %

2016-09
2016-10
2016-11
2016-12
0
20
40
60
80
100
  • 0%
  • 20%
  • 40%
  • 60%
  • 80%
  • 100%

피인용수

상세정보
저작권 정책

누리미디어에서 제공되는 모든 저작물의 저작권은 원저작자에게 있으며, 누리미디어는 각 저작물의 내용을 보증하거나 책임을 지지 않습니다. 단, 누리미디어에서 제공되는 서지정보는 저작권법에 의해 보호를 받는 저작물로, 사전 허락 없이 임의로 대량 수집하거나 프로그램에 의한 주기적 수집 이용, 무단 전재, 배포하는 것을 금하며, 이를 위반할 경우, 저작권법 및 관련법령에 따라 민, 형사상의 책임을 질 수 있습니다.

맨 위로 이동