In this study, Fe<SUB>bal.</SUB><SUB></SUB> B<SUB>16</SUB>(CeLa)<SUB>x</SUB> amorphous soft magnetic alloy ribbons with x ranging from 0 to 3.5 at.% were fabricated and the effects of Ce and La additions on their magnetic and thermal properties were analyzed. The fabricated ribbons were subjected to stress relief annealing at 375 °C for five minutes, and their microstructures were compared and analyzed using Electron Backscatter Diffraction. The saturation magnetization in the Fe<SUB>bal.</SUB>B<SUB>16</SUB> at.% ribbons decreased due to the atomic size differences among Fe, B, Ce, and La, while the coercivity stabilized at 20.75 A/m when the CeLa content exceeded 2.0 at.%. After stress relief annealing, further reductions in coercivity were observed, with the CeLa 3.5 at.% sample exhibiting the lowest coercivity of 12.74 A/m. When the CeLa content exceeded 1.5 at.%, the activation energy increased to over 515.41 kJ/mol, resulting in a stable reduction in coercivity and high thermal stability. In compositions with CeLa content of 2.0 at.% or higher crystallization did not occur, and as a result these alloys maintained low coercivity and high thermal stability and demonstrated excellent properties.
본문·목차
인공지능 문자 인식 모델을 통해 추출된 텍스트로, 일부 오타나 오류가 포함될 수 있으나 지속적으로 개선 중입니다.
오류를 발견하셨다면 해당 부분을 드래그한 후 ' 를 통해 신고해주세요.
오류를 발견하셨다면 해당 부분을 드래그한 후 ' 를 통해 신고해주세요.
최근 본 자료 전체보기