The purpose of this research was to treat the surface of zirconia via glass infiltration etching technique and estimate the effect of this etching technique on the shear bond strength of zirconia and veneering ceramic. 3 mol% Y2O3 stabilized zirconia powder and glass powder used in preparing veneering ceramic were mixed with various amounts (20, 40, 60, 80, and 100 wt%). The shear bond strength and failure mode of veneering ceramic which was produced on the etched zirconia surface were analysed. From the results of bond strength test showed that the value of 80 wt% glass group (35.52 ± 5.24 MPa) was significantly higher than that of other experimental groups (p < 0.05). The observation of fractured surfaces of experimental specimens indicated that 80 and 100 wt% glass groups showed cohesive failure and other groups illustrated adhesive and mixed failure mostly. Therefore, glass infiltration etching technique was expected to enhance the bond strength of zirconia and veneering ceramic and be feasible in clinical usage.
본문·목차
인공지능 문자 인식 모델을 통해 추출된 텍스트로, 일부 오타나 오류가 포함될 수 있으나 지속적으로 개선 중입니다.
오류를 발견하셨다면 해당 부분을 드래그한 후 ' 를 통해 신고해주세요.
오류를 발견하셨다면 해당 부분을 드래그한 후 ' 를 통해 신고해주세요.
최근 본 자료 전체보기
UCI(KEPA) : I410-ECN-0101-2015-510-002507051