The understanding and appllication of fatigue crack propagation mechanism in variable amplitude loading is very important for life prediction of the air travel structures. Particularly, the retardation and arrest behavior of fatigue crack propagation by single tension overloading is essential to the understanding and appllication of fatigue crack propagation mechanism in variable amplitude loading.
Numerous studies of the retardation behavior have been performed, however investigations of the arrest behavior have not been enough yet.
As for the arrest behavior, Willenborg had reported that the overload shut-off ratio [R<SUB>so</SUB>=(K<SUB>OL</SUB>/K<SUB>max</SUB>)<SUB>crack arrest</SUB>] had been the material constant, but recently several investigators have reported that the overload shut-off ratio depends upon the stress ratio.
In this study, authors have investigated the effect of stress ratio on the threshold overload shut-off ratio to generate arrest of fatigue crack growth in high tensile aluminum alloy 7075-T735 which have used in material for air travel structures, It has been -0.4?R?0.4 till now, the region of stress ratio investigated.
The threshold overload shut-off ratio has decreased as stress ratio has increased in overall region of -0.4?R?0.4 and the linearity has been seen in this material. Moreover, the experimental equation between R<SUB>so</SUB> and R has been made; The relation has been R<SUB>so</SUB>=-R＋2.6.
Numerous studies of the retardation behavior have been performed, however investigations of the arrest behavior have not been enough yet.
As for the arrest behavior, Willenborg had reported that the overload shut-off ratio [R<SUB>so</SUB>=(K<SUB>OL</SUB>/K<SUB>max</SUB>)<SUB>crack arrest</SUB>] had been the material constant, but recently several investigators have reported that the overload shut-off ratio depends upon the stress ratio.
In this study, authors have investigated the effect of stress ratio on the threshold overload shut-off ratio to generate arrest of fatigue crack growth in high tensile aluminum alloy 7075-T735 which have used in material for air travel structures, It has been -0.4?R?0.4 till now, the region of stress ratio investigated.
The threshold overload shut-off ratio has decreased as stress ratio has increased in overall region of -0.4?R?0.4 and the linearity has been seen in this material. Moreover, the experimental equation between R<SUB>so</SUB> and R has been made; The relation has been R<SUB>so</SUB>=-R＋2.6.
목차
Abstract
1. 序論
2. 實驗 裝置 및 方法
3. 實驗 結果 및 考察
4. 結論
參考文獻
참고문헌 (0)
참고문헌 신청함께 읽어보면 좋을 논문
논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!
-
2024-T3 A1 合金의 異方性이 疲勞龜裂進展速度와 停留擧動에 미치는 影響
한국해양공학회지
1993 .06
-
보강판의 균열거동해석과 Crack Arrest 설계(Ⅰ) - Crack Arrest 설계기준의 수치해석
한국기계가공학회지
2005 .06
-
Al 2024-T3재의 Crack Opening Point의 평가에 관한 연구
한국안전학회지
2004 .01
-
응력비 변화에 따른 혼합모드 피로균열 전파거동
대한기계학회 논문집 A권
2002 .11
-
보강판의 균열거동해석과 Crack Arrest 설계(Ⅲ) : Crack Arrest Design 차트의 실험평가
한국기계가공학회지
2006 .06
-
피로파면의 기하학적 형상을 바탕으로 한 응력진폭 변화와 혼합모드 하중관계에 관한 연구
한국자동차공학회 춘 추계 학술대회 논문집
2004 .10
-
SA-508 압력용기용강 변후재의 피로균열 Arrest 거동에 대한 변후 형상비의 영향
한국안전학회지
1991 .01
-
박판 Al 2024-T3 합금재료의 피로균열성장지연거동과 피로수명예측
한국기계기술학회지
2011 .01
-
6063-T5 알미늄 합금의 단일과대하중에 의한 부식피로균열진전거동에 관한 연구
한국안전학회지
1997 .01
-
SS41 용접재의 잔류응력장내에서의 피로균열 성장거동에 관한 연구
한국안전학회지
2002 .01
-
Crack Propagation Behavior Based on the Characteristic of the Interaction Between Two Fatigue Cracks
KSME International Journal
1998 .04
-
多重 過荷重에 의한 Al 7075-T6 合金의 疲勞龜裂 成長遲延現狀에 관한 硏究
한국해양공학회지
1992 .06
-
[論文] 고강도 알미늄 합금재에 있어서 크랙열림점 평가에 관한 연구(I)
오토저널
1993 .02
-
피로균열진전하의 하중감소에 의한 균열지연
대한기계학회 춘추학술대회
2002 .10
-
Al 2024-T3 합금재료의 두께에 따른 피로균열전파특성
한국자동차공학회 추계학술대회 및 전시회
2009 .11
-
過荷重에 의한 船舶用 알루미늄 合金材의 腐蝕疲勞 破壞遲延에 관한 硏究
한국해양공학회지
1988 .12
-
혼합모드 단일과대하중 하의 피로균열 전파거동에 관한 실험적 연구
대한기계학회 춘추학술대회
2003 .04
-
Overload 효과를 고려한 Al 5083-O 용접부 피로 수명 예측
대한용접·접합학회지
2018 .10
-
혼합모드(Ⅰ+Ⅱ)에서 피로균열진전에 미치는 응력비의 영향
한국기계가공학회지
2009 .12
-
순수 티타늄 판재의 피로균열 전파거동에 관한 연구
한국해양공학회지
1995 .06
이 논문의 저자 정보
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2009-559-015519803