The magnetic and magnetocaloric properties of Gd<SUB>1-x</SUB>Ce<SUB>x</SUB>Al<SUB>2</SUB> (x = 0, 0.25, 0.5, 0.75) intermetallic compounds alloys have been investigated in detail for the first time. XRD patterns indicated that all the samples were crystallized in a single phase with MgCu<SUB>2</SUB>-type structure (Laves phase). Ce substitution for Gd increased the lattice parameters and decreased the Curie temperature from 163 K for x = 0 to 37 K for x = 0.75. A maximum entropy change of 3.82 J/kg K was observed when a 2 T magnetic field was applied to the x = 0 sample. This entropy change decreased with increasing Ce content to 2.04 J/kg K for the x = 0.75 sample.
목차
1. Introduction
2. Experimental
3. Results and Discussion
4. Conclusions
Acknowledgements
References
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2013-428-001368951