This study was to investigate the effect of MgO addition to La2O3-Al₂O₃-SiO₂ based glass on the properties of the infiltrated glass. Several fractions of MgO (0, 0.5, 1.0, 1.5, and 2.0 wt%) were added to the La₂O₃(38-40 wt%)-Al₂O₃(19 wt%)-SiO₂(19 wt%)-B₂O₃(16 wt%)-Na₂O(4 wt%)-CaO(2 wt%) glass. Glasses were prepared by melting the appropriate mixtures of oxide powders followed by quenching in a water bath after holding at 1400℃, and then grinding into a powder using a planetary mill. The high temperature viscosity of the molten glasses was measured using high temperature viscometer according to the ASTM C-965. The glass powder-water slurry was placed on the partially sintered alumina (Accumt Mat Co., USA) preforms and infiltration was done at 1,150℃ for 20 min and then air cooled. The depth of glass infiltration in glass-alumina composites was measured using a stereomicroscope (SMZ- U, Nikon, Japan). Measurements were performed 10 times per experimental groups and averaged. The data were analyzed with one-way ANOVA. The high temperature viscosity of glass was decreased with increasing of MgO fraction. The infiltration depth in glass-alumina composite was increased with increasing of the MgO fraction (1,090±63 μm for 0% MgO, 1 ,101±24 μm for 0.5% MgO, 1 ,128±21 μm f or 1 .0% MgO, 1,168±18 μm for 1.5% MgO, and 1,214±22 μm for 2% MgO). The addition of MgO to lantanium alumino-silicate glass may improve the infiltration behavior in the preformed alumina.
목차
ABSTRACT
서론
재료 및 방법
결과
총괄 및 고안
결론
참고문헌
참고문헌 (43)
참고문헌 신청
1. [학술지(정기간행물)] - Balakrishnan A / 2009 / Mechanical properties of MgO-Al2O3-SiO2 glass-infiltrated Al2O3-ZrO2 composite / J Mater Process Tech 209 : 5271 ~ 5275
2. [학술지(정기간행물)] - Bindl A / 2002 / An u p to 5-ye ar clinical evaluation of posterior In-Ceram CAD/CAM core crowns / Int J Prosthodont 15 : 451 ~ 456
3. [학술지(정기간행물)] - Bona AD / 2008 / Characterization of glass-infiltrated alumina- based ceramics / Dent Mater 24 : 1568 ~ 1574
4. [학술지(정기간행물)] - Campbell SD / 1995 / Dimensional and formation analysis of a restorative ceramic and how it works / J Prosthet Dent 74 : 33 ~ 40
5. [학술지(정기간행물)] - Carrier DD / 1995 / In-Cerarn failure behavior and core-veneer interface quality as influenced by residual infiltration glass / J Prosthod 4 : 237 ~ 242
2. [학술지(정기간행물)] - Bindl A / 2002 / An u p to 5-ye ar clinical evaluation of posterior In-Ceram CAD/CAM core crowns / Int J Prosthodont 15 : 451 ~ 456
3. [학술지(정기간행물)] - Bona AD / 2008 / Characterization of glass-infiltrated alumina- based ceramics / Dent Mater 24 : 1568 ~ 1574
4. [학술지(정기간행물)] - Campbell SD / 1995 / Dimensional and formation analysis of a restorative ceramic and how it works / J Prosthet Dent 74 : 33 ~ 40
5. [학술지(정기간행물)] - Carrier DD / 1995 / In-Cerarn failure behavior and core-veneer interface quality as influenced by residual infiltration glass / J Prosthod 4 : 237 ~ 242
함께 읽어보면 좋을 논문
논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!
-
글라스의 MgO 함량이 글라스-알루미나 복합체의 물성에 주는 영향
대한치과재료학회 학술대회
2009 .04
-
지르코니아-유리복합체용 글래스의 조성에서 MgO의 함량 변화가 강도에 미치는 영향
대한치과기공학회지
2007 .01
-
CaO·MgO·2SiO₂-3CaO·P₂O5-MgO·TiO₂계 Glass-Ceramic의 기계적 성질에 관한 연구(Ⅱ)
대한치과재료학회지
1996 .12
-
CaO·MgO·2SiO₂-3CaO·P₂O5-MgO·TiO₂계 Glass-Ceramic의 세포독성 평가(Ⅲ)
대한치과재료학회지
1996 .12
-
유리의 조성에서 MgO, Li₂O 및 ZrO₂의 함량변화가 유리침투 알루미나 세라믹 재료의 강도와 색조의 변화에 미치는 영향
대한치과재료학회지
2002 .09
-
MgO-CeO₂-Y₂O₃의 함량변화가 유리침투 알루미나 코어 세라믹의 강도와 색조 변화에 미치는 영향
대한치과재료학회지
2001 .12
-
치관보철용 $CaO-MgO-SiO_{2}-P_{2}O_{5}-TiO_2$계 글라스 세라믹의 결정화와 기계적 물성에 미치는 열처리 조건의 영향
대한치과기공학회지
2004 .01
-
유리의 조성에서 MgO-ZrO₂-MnO의 함량변화가 유리침투 알루미나 코어 세라믹의 강도와 색조의 변화에 미치는 영향
대한치과재료학회지
2001 .09
-
지르코니아 세라믹의 Glass-infiltration에 의한 2축 굽힘강도에 관한 연구
대한치과기공학회지
2008 .01
-
치과용 부가중합형 실리콘 인상재에 대한 MgO-CaO-Al₂O₃-SiO₂계 고강도 글라스 필러의 효과
대한치과재료학회지
2005 .03
-
치과용 친수성 부가중합형 실리콘 인상재에 대한 MgO-CaO-Al₂O₃-SiO₂계 고강도 글라스 필러의 효과
대한치과재료학회 학술대회
2005 .02
-
용융침투법에 의한 알루미나-유리 복합체의 개발에 대한 연구
대한치과재료학회지
1999 .03
-
Phosphate Based Glasses for Hard and Soft Tissue Surgery
대한치과재료학회 학술대회
2011 .05
-
치관 보철용 CaO-MgO-$SiO_2-P_2O_5-TiO_2$계 글라스 세라믹의 합성과 경도
대한치과기공학회지
1999 .01
-
Zirconia-Frit composites의 소결 및 물성에 미치는 MgO 첨가의 효과
대한치과기공학회지
2010 .01
-
이트리아 첨가 붕규산염 유리로 제조한 알루미나-유리 복합체의 강도 평가
대한치과재료학회지
1998 .06
-
이트리아 첨가 붕규산염 유리로 제조한 알루미나-유리 복합체의 파괴인성 평가
대한치과재료학회지
1998 .09
-
용융침투법으로 제조한 알루미나-유리 복합체의 동적 피로 특성 평가
대한치과재료학회지
1998 .12
-
Biocompatibility of 3D-Printed PCL/HAp/MgO Composite Scaffolds Modified by Plasma Etching
대한치과재료학회 학술대회
2016 .11
이 논문의 저자 정보
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2015-510-001091361