Interfacial degradation of thermal barrier coatings in isothermal and cyclic oxidation tests

전설; 이희수; 최영규; 신현규; 정영근

추천

검색

자료유형: 학술저널

저자정보: 전설 이희수 최영규 신현규 정영근

저널정보: 한국결정성장학회 한국결정성장학회지 한국결정성장학회지 제24권 제4호

발행연도: 2014.1

수록면: 151 - 157 (7page)

이용수

📌

연구주제

📖

연구배경

🔬

연구방법

🏆

연구결과

초록· 키워드

오류제보하기

The degradation mechanisms of thermal barrier coatings (TBCs) were investigated in different thermal fatiguecondition in terms of microstructural analyses. The isothermal and cyclic oxidation tests were conducted to atmosphericplasma sprayed-TBCs on NIMONIC 263 substrates. The delamination occurred by the oxide layer formation at theinterface, the Ni/Cr-based oxide was formed after Al-based oxide layer grew up to ~10 μm in the isothermal condition. Inthe cyclic oxidation with dwell time, the failure occurred earlier (500 hr) than in the isothermal oxidation (900 hr) at sametemperature. The thickness of Al-based oxide layer of the delaminated specimen in the cyclic condition was ~4 μm and theinterfacial cracks were observed. The acoustic emission method revealed that the cracks generated during the cooling step. It was considered that the specimens were prevented from the formation of the Al-based oxide by cooling treatment, andthe degradation mode in the cyclic test was dominantly interfacial cracking by the difference of thermal expansioncoefficients of the coating layers.

#Thermal barrier coating #Thermal fatigue condition #Oxide layer growth #Crack propagation #Degradation mechanism

참고문헌 (25)

참고문헌 신청

A. Afrasiabi / 2008 / A comparativestudy on hot corrosion resistance of three types ofthermal barrier coatings: YSZ, YSZ +Al2O3 and YSZ/Al2O3 / Mat. Sci. Eng. A 478 : 264 ~

A.C. Fox / 2004 / Oxygen transport by gaspermeation through the zirconia layer in plasma sprayedthermal barrier coatings / Surf. Coat. Technol 184 : 311 ~

A.G. Evans / 2001 / Mechanisms controlling the durabilityof thermal barrier coatings / Prog. Mater. Sci : 505 ~

A.G. Evans / 2001 / Mechanisms controlling the durabilityof thermal barrier coatings / Progress in Mater. Sci 46 : 505 ~

A.M. Limarga / 2011 / Stress distributionsin plasma-sprayed thermal barrier coatingsunder thermal cycling in a temperature gradient / J. Appl. Mech 78 : 011003 ~ 011001