The holding time during solution heat treatment of unstabilized austenitic stainless steels as specified in the nuclear regulatory requirements was investigated. The sensitized 2.54㎝ thick specimens held at 675℃ for 1 h were rejected by ASTM A262 test, due to the large amount of chromium carbide precipitated in the form of 50~300㎚ particles at the grain boundaries. They also showed about 10.8% of DOS in the DL-EPR test. However, solution heat treatment of the sensitized specimens at 1,038℃ and 1,121℃ for at least 1 min resulted in the complete dissolution of chromium carbide into the grains, and they passed ASTM A262 test and showed less than 0.01% of DOS in the DL-EPR test. As a result of solution heat treatment at 1,038℃ for 5 h of the 25.4㎝ thick specimen sensitized at 675℃ for 10 h, it passed ASTM A262 and DL-EPR test at any position in the specimen thickness. While the specimen surface showed a step structure without the precipitation of chromium carbide and a DOS less than 0.01%, towards the center, a dual structure was observed. It exhibited about 0.6% of DOS due to the longer exposure time to the sensitization range of 427~816℃. Considering the minimum time in which the chromium carbide precipitated at the grain boundary at 1,038℃ was completely dissolved into the grain, and the maximum delay time for the center of the specimen to reach 1,038℃ rather than the surface, the holding time for complete solution heat treatment to the center was found to be up to 2 min per 2.54㎝ of material thickness. The solution heat treatment for 0.5~1.0 h per 2.54㎝ of material thickness at 1,038~1,121℃, which is employed in the nuclear power industry, was proven to prevent grain boundary corrosion by inhibiting the sensitization of unstabilized austenitic stainless steels.
목차
Abstract
1. Introduction
2. Experimental Method
3. Test Results and Discussion
4. Conclusion
References
참고문헌 (12)
참고문헌 신청
Sehwa editorial department / 1992 / Stainless Steel Handbook / Sehwa :60~69
2019 / Setion II Part A & D of ASME Boiler and Pressure Vessel Code / The American Society of Mechanical Engineers (ASME)
정병호 / 2006 / 316 스테인리스강의 입계부식에 미치는 열사이클과응력의 영향 / 한국마린엔지니어링학회지 30(6):709~715
2014 / ASTM A262, Standard Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels / American Society for testing and materials (ASTM)
1994 / ASTM G108, Standard Test Method for Electrochemical Reactivation (EPR) for Detecting Sensitization of AISI Type 304 and 304L Stainless Steels / American Society for testing and materials (ASTM)
2019 / Setion II Part A & D of ASME Boiler and Pressure Vessel Code / The American Society of Mechanical Engineers (ASME)
정병호 / 2006 / 316 스테인리스강의 입계부식에 미치는 열사이클과응력의 영향 / 한국마린엔지니어링학회지 30(6):709~715
2014 / ASTM A262, Standard Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels / American Society for testing and materials (ASTM)
1994 / ASTM G108, Standard Test Method for Electrochemical Reactivation (EPR) for Detecting Sensitization of AISI Type 304 and 304L Stainless Steels / American Society for testing and materials (ASTM)
함께 읽어보면 좋을 논문
논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!
-
비안정화 오스테나이트계 스테인리스강의 입계부식에 미치는 용체화열처리 유지시간의 영향
대한용접·접합학회지
2020 .06
-
시효열처리 및 UNSM 처리에 따른 316L 스테인리스강의 입계부식거동
Corrosion Science and Technology
2015 .01
-
Austenitic Stainless Steel 배관의 온도에 따른 환경 피로 영향
대한기계학회 춘추학술대회
2019 .04
-
Intergranular Corrosion Mechanism of Slightly-sensitized and UNSM-treated 316L Stainless Steel
Corrosion Science and Technology
2016 .01
-
이음매 없는 304L 스테인리스강관의 부식특성에 미치는 열처리의 영향
Corrosion Science and Technology
2017 .01
-
Ductility and Fatigue Properties of Type 316L Austenitic Stainless Steel after Thermal Pre-charging with Hydrogen
대한기계학회 춘추학술대회
2019 .04
-
304 스테인리스강 용접 열영향부의 입계 부식에 미치는 탄소함량의 영향
대한용접·접합학회지
2019 .08
-
Evaluation of Sensitization Behaviors on the Heat-Affected Zone of Austenitic Stainless Steel Weld by Thermal Cycles of Multi-pass Welding
대한용접학회 특별강연 및 학술발표대회 개요집
2024 .10
-
F316 오스테나이트 스테인리스강의 상변태 및 입계부식저항성에 미치는 입열의 영향
Corrosion Science and Technology
2020 .01
-
냉간가공을 통한 중성자조사된 오스테나이트 스테인리스강의 기계적물성 모사 타당성 분석
한국압력기기공학회 논문집
2019 .12
-
304L 스테인리스강의 열처리에 따른 입계부식민감도 연구
Corrosion Science and Technology
2020 .01
-
Effect of Carbon Content and Welding Heat Input on the Heat Affected Zone of 304 Stainless Steel
대한용접학회 특별강연 및 학술발표대회 개요집
2018 .11
-
재료시험에 의한 탄소강(SS275)과 오스테나이트계 스테인리스강(STS316)의 기계적 성질 조사
대한건축학회 학술발표대회 논문집
2021 .10
-
슈퍼오스테나이트 스테인리스강의 순환동전위 분극특성에 미치는 해수온도의 영향과 손상 거동에 관한 미시적 분석
Corrosion Science and Technology
2021 .12
-
레이저 및 TIG 용접된 오스테나이트계 스테인리스강의 기계적 특성에 대한 연구
동력시스템공학회지
2019 .04
-
스테인레스강 SS420의 입계예민화에 의한 피트 부식
한국재료학회지
2017 .01
-
Novel Austenitic Stainless Steel with Advanced Mechanical Properties Fabricated by Selective Laser Melting of Powder Mixture of Austenitic and Ferritic Stainless Steels
한국정밀공학회 학술발표대회 논문집
2021 .11
-
슈퍼 오스테나이트 스테인리스강 조관 용접부 내식성 영향 인자 연구
대한용접학회 특별강연 및 학술발표대회 개요집
2017 .11
-
열화된 스테인리스강의 마모특성에 관한 연구
동력시스템공학회지
2017 .12
이 논문의 저자 정보
최근 본 자료
댓글(0)
0
UCI(KEPA) : I410-ECN-0101-2020-581-000842277