$SnO_2$-mixed and Sn-doped $TiO_2$ nanoparticles were synthesized via a hydrothermal process. $SnO_2$-mixed $TiO_2$ nanoparticles prepared in a neutral condition consisted of anatase $TiO_2$ nanoparticles(diamond shape, ~25 nm) and cassiterite $SnO_2$ nanoparticles(spherical shape, ~10 nm). On the other hand, Sn-doped $TiO_2$ nanoparticles obtained under a high acidic condition showed a crystalline phase corresponding to rutile $TiO_2$. As the Sn content increased, the particle shape changed from rod-like(d~40 nm, 1~200 nm) to spherical(18 nm) with a decrease in the particle size. The peak shift in the XRD results and a change of the c-axis lattice parameter with the Sn content demonstrate that the $TiO_2$ in the rutile phase was doped with Sn. The photocatalytic activity of the $SnO_2$-mixed $TiO_2$ nanoparticles dramatically increased and then decreased when the $SnO_2$ content exceeded 4%. The increased photocatalytic activity is mainly attributed to the improved charge separation of the $TiO_2$ nanoparticles with the $SnO_2$. In the case of Sn-doped $TiO_2$ nanoparticles, the photocatalytic activity increased slightly with the Sn content due most likely to the larger energy bandgap caused by Sn-doping and the decrease in the particle size. The $SnO_2$-mixed $TiO_2$ nanoparticles generally exhibited higher photocatalytic activity than the Sn-doped $TiO_2$ nanoparticles. This was caused by the phase difference of $TiO_2$.
목차
등록된 정보가 없습니다.
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
최근 본 자료
댓글(0)
0