NaNbO₃:Eu<SUP>3+</SUP> phosphor thin films were grown on quartz substrates by radio-frequency magnetron sputtering at a growth temperature of 100 ℃, with subsequent annealing at temperatures of 800, 900, and 1000 ℃. The effects of annealing temperature on the structural, morphological, and optical properties of the thin films were investigated. The NaNbO₃:Eu<SUP>3+</SUP> sputtering target was synthesized by a solid-state reaction of raw materials Na₂CO₃, Nb₂O₅, and Eu₂O₃. The X-ray diffraction patterns exhibited that the thin films had two mixed phases of NaNbO₃ and Eu₂O₃. Surface morphologies were investigated by using field emission-scanning electron microscopy and indicated that the grains of the thin film annealed at 1000 ℃ showed irregular shapes with an average size of approximately 300 ㎚. The excitation spectra of Eu<SUP>3+</SUP>-doped NaNbO₃ thin film consisted of a strong charge transfer band centered at 304 ㎚ in the range of 240–350 ㎚ and two weak peaks at 395 and 462 ㎚, respectively, resulting from the ⁷F₀→⁵L₆ and ⁷F0→⁵H₂ transitions of Eu<SUP>3+</SUP> ions. The emission spectra under excitation at 304 ㎚ exhibited an intense red band centered at 614 ㎚ and two weak bands at 592 and 681 ㎚. As the annealing temperature increased from 800 ℃ to 1000 ℃, the intensities of all the emission bands and the band gap energies gradually increased. These results indicate that the higher annealing temperature enhance the luminescent properties of NaNbO₃:Eu<SUP>3+</SUP> thin films.
목차
Abstract
1. 서론
2. 실험
3. 결과 및 고찰
4. 결론
References
참고문헌 (16)
참고문헌 신청
T. Koide, M. Ito, T. Kawai, Y. Matsushima, An Inorganic Electroluminescent Device Using Calcium Phosphate Doped with Eu3+ as the Luminescent Layer, Mater. Sci. Eng. B, 178 (2013) 306-310.
J. Fan, C. Yu, C. Qian, X. Fan, G. Zhang, Thermal/luminescence Characterization and Degradation Mechanism Analysis on Phosphor-Converted White LED Chip Scale Packages, Microelectron. Reliab. 74 (2017) 179-185.
Z. Wang, X. Zhao, Z. Guo, P. Miao, X. Gong, Carbon Dots Based Nanocomposite Thin Film for Highly Efficient Luminescent Solar Concentrators, Org. Electron. 62 (2018) 284-289.
D. Alami, Environmental Applications of Rare-Earth Manganites as Catalysts: A Comparative Study, Environ. Eng. Res. 18(4) (2013) 211-219.
R. Krishnan, H. C. Swart, J. Thirumalai, P. Kumar, Depth Profiling and Photometric Characteristics of Pr3+ Doped BaMoO4 Thin Phosphor Films Grown Using (266 nm Nd-YAG laser) Pulsed Laser Deposition, Appl. Surf. Sci. 488 (2019) 783–790.
J. Fan, C. Yu, C. Qian, X. Fan, G. Zhang, Thermal/luminescence Characterization and Degradation Mechanism Analysis on Phosphor-Converted White LED Chip Scale Packages, Microelectron. Reliab. 74 (2017) 179-185.
Z. Wang, X. Zhao, Z. Guo, P. Miao, X. Gong, Carbon Dots Based Nanocomposite Thin Film for Highly Efficient Luminescent Solar Concentrators, Org. Electron. 62 (2018) 284-289.
D. Alami, Environmental Applications of Rare-Earth Manganites as Catalysts: A Comparative Study, Environ. Eng. Res. 18(4) (2013) 211-219.
R. Krishnan, H. C. Swart, J. Thirumalai, P. Kumar, Depth Profiling and Photometric Characteristics of Pr3+ Doped BaMoO4 Thin Phosphor Films Grown Using (266 nm Nd-YAG laser) Pulsed Laser Deposition, Appl. Surf. Sci. 488 (2019) 783–790.
함께 읽어보면 좋을 논문
논문 유사도에 따라 DBpia 가 추천하는 논문입니다. 함께 보면 좋을 연관 논문을 확인해보세요!
-
기판 및 열처리 온도에 따른 SrWO<sub>4</sub>:Dy<sup>3+</sup>, Eu<sup>3+</sup> 형광체 박막의 특성
한국재료학회지
2016 .01
-
증착 온도에 따른 Ca₂SrAl₂O6:Eu3+ 형광체 박막의 특성
한국표면공학회 학술발표회 초록집
2019 .11
-
열처리 온도 변화에 따른 라디오파 마그네트론 스퍼터링으로 성장된 MgMoO₄:Eu3+ 형광체 박막의 특성
Current Photovoltaic Research
2016 .03
-
서로 다른 증착 온도에서 성장된 BaWO₄:Sm3+ 형광체 박막의 구조, 광학, 표면 형상의 특성
한국표면공학회지
2022 .04
-
백색 LED를 위한 형광체 발전
한국표면공학회 학술발표회 초록집
2015 .11
-
Luminescence Properties of Ba₃Si6O12 N₂:Eu2+ Green Phosphor
한국표면공학회지
2015 .10
-
CaWO₄:Eu3+ 적색 형광체 분말과 박막의 제조와 발광 특성
한국표면공학회 학술발표회 초록집
2019 .11
-
BaWO₄:Dy3+,Eu3+ 백색광 형광체의 발광 특성과 에너지 전달 효율
한국표면공학회지
2021 .06
-
Synthesis and Characterization of Soluble Polyaniline and TiO2 Composite
Current Photovoltaic Research
2015 .09
-
BaSiO<sub>3</sub>:RE<sup>3+</sup> (RE = Sm, Eu) 형광체의 합성과 광학 특성
한국재료학회지
2019 .01
-
Investigation of thermal annealing effects on the optical transparency and luminescent characteristics of Eu-doped Y2O3 thin films
Journal of Ceramic Processing Research
2019 .01
-
메틸계 실리콘 수지 기반 형광체막 성형에 따른 특성 비교
한국정밀공학회 학술발표대회 논문집
2016 .05
-
주형법으로 제조된 Gd<sub>2</sub>O<sub>3</sub>:Eu<sup>3+</sup> 적색 형광체의 나노입자 분산 및 형상제어
한국재료학회지
2017 .01
-
CaAl<sub>2</sub>O<sub>4</sub>:RE<sup>3+</sup>(RE = Tb, Dy) 형광체의 발광 특성
한국재료학회지
2016 .01
-
활성제 이온의 농도 변화에 따른 La₂MoO6:RE3+ (RE = Eu, Sm) 형광체의 발광 특성
한국표면공학회지
2017 .08
-
적색 형광체 신뢰성 향상을 위한 코팅 형광체의 고진공 조건 열처리에 관한 연구
조명·전기설비학회논문지
2020 .02
-
IMPACT OF HIGH TEMPERATURE AND SHORT PERIOD ANNEALING ON SnS FILMS DEPOSITED BY E-BEAM EVAPORATION
AFORE
2015 .11
-
Effect of annealing on physical properties of E-beam deposited SnS films
한국신·재생에너지학회 학술대회 초록집
2015 .11
-
BiNbO4:RE3+ (RE = Dy, Eu, Sm, Tb) 형광체의 광학 특성
한국표면공학회지
2017 .06
-
Glass Remote Phosphor 구조를 갖는 백색 LED 패키지의 형광체 함량과 열처리 온도 최적화
조명·전기설비학회논문지
2016 .03
이 논문의 저자 정보
최근 본 자료
댓글(0)
0