In this study, the effect of the microstructure and mechanical properties of austempered high-carbon (0.9%C) high-silicon (2.3 %Si) cast steel were investigated. The specimens were austenitised for 60 min. at 900 °C, and austempered at 260 °C, 320 °C, and 380 °C for periods of time ranging from 30 min to 240min. After receiving this heat treatment, the mechanical properties were measured using both a tensile test and hardness test. To analyze the microstructure, an optical microscope was used and an X-ray diffraction (XRD) analysis was carried out. In this study, high carbon high silicon cast steel without graphite and with higher tensile strength (1300 MPa to 2200 MPa) and elongation (~25 %), when compared to austempered ductile cast iron (ADI), was developed. When the austempering temperature was at 260 °C, the microstructures were low ausferrite, but at 380 °C, an upper ausferrite structure was formed. As the austempering temperature increased from 260 to 380 °C, the ultimate tensile strength and hardness decreased, but the elongation and retained austenite volume fraction increased. In addition, the microstructures were coarser.
목차
등록된 정보가 없습니다.
참고문헌 (0)
참고문헌 신청이 논문의 저자 정보
최근 본 자료
댓글(0)
0